Electrode, Welding, Welding Electrode manufacturer / supplier in China, offering Free Sample! Cobalt-Based Rod/Wire/Electrode Stellite 22, Tungsten Electrode Wt20 for TIG Welding, Wt20 Tungsten Welding Electrode Dayang Brand and so on.

Gold Member Since 2006
Audited Supplier

Free Sample! Cobalt-Based Rod/Wire/Electrode Stellite 22

Get Latest Price
Min. Order / Reference FOB Price
10 Kilograms US $30-35/ Kilograms
Port: Shanghai, China
Production Capacity: 300 Metric Ton/Metric Tons Per Month
Payment Terms: L/C, T/T
Type: L (Low Temperature Low Alloy Steel Electrode)
Material: Tungsten
Diameter: 3.2/4.0/5.0mm
Length: 350mm
Welding Core Type: Cobalt Chromium Tungsten Alloy Cores
Electrode Coating Type: Titanium Calcium

You Might Also Like

Loading...

Basic Info

Model NO.
Stellite 22
Slag Characteristic
Alkaline
Welding Power
AC or DC+
Trademark
Ocean Welding
Transport Package
5kg/Box, 20kg/Carton
Origin
Zhejiang, China(Mainland)
Free Sample!Cobalt-Based Rod/Wire/Electrode Stellite 22
is a titanium calcium type coating, surfacing electrode with cobalt chromium tungsten alloy cores, should adopt DCRP. Surfacing metal can keep good abrasion resistance and corrosion resistance at 650 degrees.

Applications:
used in the work of 650 degrees Celsius should be able to maintain good wear resistance and a certain degree of corrosion resistance of the occasion; for example, the high temperature and high pressure welding valve and hot shear knife, the impact of hot and cold staggered place.
Chemical Composition of the deposited metal
 
AlloyNominal Analysis of Welding ElectrodeOtherUNSASME/AWSHardness(HRC)
CoCrWCNiMoFeSi
Cobalt Base Alloy Bare Welding Electrodes
Stellite1Bal.32122.45≤3≤1≤3≤2≤0.5R30001(SF)A5.21
ERCoCr-C
51-56
Stellite6Bal.304-51.2≤3≤1≤3≤2≤0.5R30006(SF)A5.21
ERCoCr-A
40-45
Stellite12Bal.3081.4-1.8≤3≤1≤3≤2≤0.5R30012(SF)A5.21
ERCoCr-B
46-51
Stellite20Bal.33162.45≤3≤1≤3≤2≤0.5--53-59
Stellite21Bal.28-0.2535.2≤3≤1.5≤0.5R30021(SF)A5.21
ERCoCr-E
28-40*
Stellite22Bal.28-0.31.512≤3≤2≤0.5--41-49*
Stellite25Bal.20140.110≤1≤3≤1≤0.5--20-45*
Stellite31Bal.267.50.510-≤2≤1≤0.5R30031-20-35*
StelliteFBal.26121.722≤1≤3≤2≤0.5R30002(SF)A5.21
ERCoCr-F
40-45
Stellite107Bal.314224-≤2≤3≤0.5--38-47
Stellite190Bal.2713.53.2≤1≤1≤31≤0.5R30014(SF)A5.21
ERCoCr-G
54-59
Stellite250Bal.28-0.1--21≤1≤0.5--20-28
Stellite306Bal.2530.56-416%Nb--32-42*
Stellite694Bal.281915-≤311&V--48-54
AlloyNominal Analysis of Welding ElectrodeOthersUNSASME/AWSHardness(HRC)
CoCrWCNiMoFeSi
Cobalt Base Alloy Bare Welding Electrodes
Stellite706Bal.31-1.2≤34≤3≤1≤1--39-44
Stellite712Bal.31-1.5/1.9≤38≤3≤2≤1--46-51
ULTIMETBal.2620.06953-≤1R31233-28-45*


Electrode specification and reference current (AC or DC+):
Diameter(mm)3.24.05.0
Length(mm)350350350
Current(A)120-160140-190150-210

Notes:
1: before welding electrode must be 150 degrees bake for 1 hours
2: according to the size of the tool and the type of parent material, must be preheated by 300-600 DEG C, should use small current short arc welding
3: after welding should be tempered at 600-700 DEG C after 1 hours and then cold or immediately put the workpiece into the dry and hot sand box or plant ash in the cold, so as not to crack.

Contact Us:
 
TEL:86 0571 87169872
 
 
 

 

Send your message to this supplier

*From:
*To:
avatar Miss Yuki
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now