Aws Eni-Ci Cast Iron Electrod

• Type: C (Cast Iron Welding Rod)
• Material: Cast Iron
• Diameter: 2.5mm 3.2mm 4.0mm
• Length: 300-400mm
• Welding Core Type: Alloy Structural Steel
• Electrode Coating Type: Titanium
• Model NO.: AWS ENi-CI
• Slag Characteristic: Alkaline
• Stainless Steel Welding Rod Type: Chromium Nickel Stainless Steel
• Function: Surfacing Electrode, Hardfacing Electrode, High Efficient Iron Powder Electrode, Gravity Electrode, Moisture-Proof Electrode
• Welding Power: AC/DC
• Application: All Grades of Castings, Pumps Casing,
• Delivery for Welding Solder: 20-25days
• Welding Current: International Standard
• Operating Current: International Standard
• Operating Temperatur: International Standard
• Company History: 27 Years
• MOQ: 500kgs
• Quality: High Level
• Welding Performance: Excellent
• Standard: Aws CE
• Certificate: with CE and ISO Certificates
• Service: Best After-Sales Service
• History: 26 Years
• Payment Term: All Terms
• Address: Hangzhou City
• Transport Package: 5kgs/Box, 20kgs/Carton
• Specification: 2.0/2.5/3.0/4.0
• Trademark: Ocean Welding
• Origin: Zhejiang, China (Mainland)
• HS Code: 8311200000
• Production Capacity: 200 Ton/Tons Per Month for Solder

Product Description

Product Description

Cast Iron Welding Electrode / Solder (AWS ENi-C1)
DESCRIPTION:
        AWS ENi-C1 is a covered welding electrode with pure nickel core and graphitic coating for cast iron.The weld seam metal has excellent machinability and crack resistibility.Both AC and DC can be applied.

APPLICATION:
       It is used for repair welding thin pieces and processing surface of cast iron,as well as important gray cast iron pieces,such as engine gear box,machining tools,guideway,etc.

ATTENTION:

1. Welding electrodes must be baked for 1hour at the temperature of 80-120ºC before welding.
2. Hammering the welded seam to dispel stress around the welding region and to avoid cracking.
3. Large current should be avoided in cold welding for cast iron,so as to reduce impurities of base metal to penetrate the weld seam and to reduce the width of the weld zone,and then to improve the ability of crack-resistance and capability of machine processing of the weld seam.

Details about Cast Iron Welding Electrode / Solder
   Place of Origin: Zhejiang China (Mainland)
   Brand Name: Ocean Welding
   Model Number: ENi-C1
   Material: Cast Iron
   Length: 300mm-500mm
   Diameter: 2.0mm,2.5mm,3.2mm,4.0mm
   Color: grey-white
   Application: repair welding on the flaws of gray cast iron, repair welding

Specifications
    Cast Iron Electrode ,welding electrode, repair welding of defects grey cast iron.
    Cast iron welding electrode is made by Ni cored stick, it is used for Joint welding of grey cast iron,temper cast iron,nodular cast iron as well as joint welding of cast iron with steel,stainless steel and Monel metal. Our cast iron products are included AWS ECI .ENI-CI, ENIFE-CI, ENICU-B.

Features
   1) Pure nickel core
   2) Strong reducing property
   3) Graphite type welding rod
   4) Weldment: no need to preheat, good crack resistibility and process-ability
   5) Both AC and DC applicable
   6) Relatively expensive
   7) Used for welding thin cast iron piece and repairing welding surfaces, such as the cast iron parts of cylinder covers, engine bases, gearcases and lathe guide rails