3.2mm Welding Electrodes E6013 with High Quality

Product Description

Product Description

   Heat-resisting Steel Electrode AWS E6013
           E6013 is a carbon steel electrode of high titanium potassium type coating. AC and DC, can be used for all-position welding, good operation performance, easy arc ignition, suitable for welding low carbon steel structure, especially suitable for intermittent welding of small and short welds and smooth surface welding
     1. Details about the Round Solid Rod
          Place of Origin: Zhejiang, China (Mainland)
          Brand Name: Ocean Welding/Dayang
          Model Number: E6013
          Material: Steel Alloy
          Length: 300mm 350mm 400mm 450mm
          Diameter: 2.0mm,2.5mm,3.2mm,4.0mm

     2. Descriptions
         Pearlitic heat-resisting steel with coating of low sodium hydrogen electrode.DC reverse connection and all position welding.Workpiece shall be preheated about 150-250°C before welding and tempering at 620-710°C after welding process.  
 
     3. Features
         1) Welding temperature is lower than 300 degrees
         2) Heat-resistant-Steel-Electrode

     4. Inner packing
         1) 2.5mm x 300mm, 1-5kg/inner box + plastic bag 
         2) 3.2mm x 350mm, 1-5kg/inner box + plastic bag
         3) 4.0mm x 350mm, 1-5kg/inner box + plastic bag
                                
    Deposited metal diffusion hydrogen content:≤6.0ml/100g (Method of glycerol)
       X ray flaw detection requirement:LevelI

    Reference Current:(DC)                                                                                                
         Diameter (mm)             Φ3.2                   Φ4.0                    Φ5.0                              
         Current (A)                     90-120              140-180              170-210                       
    Notes:
         (I)Please bake WER107 Heat-resistant Steel Electrode for 1 hour at about 350°C before welding.(II)Clean the surface to be welded thoroughly to remove surface contaminations.
     Company Information
          Hangzhou Lin'an Dayang Welding Material Co., Ltd., located in the western part of Hangzhou, was established at the beginning of this century. We possess a production line of oil pressure unit, which can produce 5000 ton stainless steel welding electrodes. Our company owns rich technical resources to design, research and mainly produce special type of electrodes with complete models. 
          The electrodes are mainly exported and the amount is up to 2000 tons per year on average. Our customers are mainly from Germany, Indonesia, Singapore, Philippines, Vietnam, Thailand, Bengal, and Egypt. They think highly of our products all the time. 
          In the days of 21st century, we will be stricter with ourselves and have continuous technical innovation which will spur us on to higher quality products for our users. Customers at home and abroad are sincerely invited to visit, call and hold talks on internet.

Carbon steel welding electrodes
Item NO.			GB/TB			AWS
J421			E4313			E6013
Description:       Pearlitic heat-resisting steel with coating of low sodium hydrogen electrode. DC reverse connection and  all  position welding. Workpiece shall be preheated about 150-250°C before welding and  tempering at 620 710°C after welding  process.
Application:       WER107 Heat-resistant Steel Electrode apply to weld the covering of the boiler pipes  (e.g.15Mo) after argon arc render with working temperature below 510°C. Can also apply to weld  general high strength  low alloy steel.
Chemical composition of Deposited metal(%):
C	Mn	Si	Mo	P	S---
≤0.12	≤0.90	≤0.60	0.40-0.65	≤0.035	≤0.035
Mechanical Performance of deposited Metal(690±15°C×1H tempering)
Rm(Mpa)		ReL(Mpa)		A(%)		Akw(J)
≥490		≥390		≥22		normal temperature
						≥27
Deposited metal diffusion hydrogen content:≤6.0ml/100g (Method of glycerol) X ray flaw detection requirement:LevelI
Reference Current:(DC)
Diameter (mm)	Φ3.2			Φ4.0			Φ5.0
Current (A)	90-120			140-180			170-210
Notes:       (I)Please bake WER107 Heat-resistant Steel Electrode for 1 hour at about 350°C before welding.       (II)Clean the surface to be welded thoroughly to remove surface contaminations